Akcaozoglu, KubilayKilli, Adem2024-11-072024-11-0720210718-915Xhttps://doi.org/10.7764/RDLC.20.1.37https://hdl.handle.net/11480/13976In this study, the effect of curing conditions on the mechanical properties of slurry infiltrated fiber reinforced concrete (SIFCON) was investigated. For this purpose, SIFCON samples containing 4% and 8% steel fiber with two different aspect ratios were produced. The samples were subjected to three different curing types, namely standard, dry and accelerated curing methods. Ultrasonic wave velocity, flexural strength, fracture toughness, compressive strength, impact resistance and capillary water absorption tests were performed on the samples. The highest flexural strength was found to be achieved in the samples with an aspect ratio of 55 and a content of 8% steel fiber. The most suitable curing method was determined as the standard curing method and the best flexural strength was achieved at the rate of 8%. According to the test results, the best strength properties were achieved in the samples exposed to the standard curing method. In addition, the samples exposed to the accelerated curing method showed satisfactory values. The accelerated curing method can be used as an alternative in SIFCON production especially in applications requiring mass production.eninfo:eu-repo/semantics/openAccesscapillary water absorptioncompressive strengthcuring conditionsflexural strengthimpact resistanceSIFCONArticle201375110.7764/RDLC.20.1.372-s2.0-85106590060N/AWOS:000654241200004Q4