Alrjaibi A.Bayol E.Kandemirli F.2019-08-012019-08-0120191452-3981https://dx.doi.org/10.20964/2019.03.44https://hdl.handle.net/11480/1559This examination researched the impact of changing measures of 4-(4-bromophenyl) Thiosemicarbazide (4-BrPhTSC) by assessing air conditioning impedance and AC and flow potentiometry in a 1 M HCl arrangement at 20°C. In an unlimited arrangement, when the E corr value is - 0.518 V, the concentration of the inhibitor solution changes and the grouping of the inhibitor changes. The present's thickness of the anodic and cathodic districts is bring down contrasted with that of the 1.0 M HCl arrangement, with an I corr estimation of 158.78 µA.cm -2 in the uninhibited arrangement and 8.10 µA.cm -2 at the 1x10 -2 M concentration of 4-BrPhTSC. It very well may be seen that as the grouping of the inhibitor builds, the consumption current thickness value diminishes, and the restraint productivity value likewise increments. The percent restraint proficiency extended from 71% to 95%. For the uninhibited and most astounding grouping of 4-BrPhTSC arrangement, the estimations of Rp blank and Rp inh were 235 and 2006 ?cm-2, separately, CPE blank and CPE inh were 348 and 36 µF.cm -2 , individually, n blank and n inh were 0.94 and 0.84. As the Rp esteem builds, the CPE esteem and n diminish as the inhibitor focus increments, potentially because of abatement in neighborhood dielectric steady or an expanded thickness at the metal/arrangement interface. The adsorption of the inhibitor on the surface of the low carbon steel fits in with the Langmuir show. Also, the adsorption harmony steady and the adsorption free vitality were evaluated. For the subsidiaries of 4-BrPhTSC, the estimation of ?Go ads and is - 36.00 kJ mol -1 , demonstrating that the adsorption of these inhibitors includes two sorts of communications: physical adsorption and chemisorption. The thickness utilitarian hypothesis (DFT) of the B3LYP work with the 6-311G (d,p) premise set was performed on 4-BrPhTSC as appeared in Table 1, Table 2. © 2019 The Authors.eninfo:eu-repo/semantics/openAccessCorrosionInhibitionLow carbon steelQuantum chemistry researchThiosemicarbazideArticle1432526253810.20964/2019.03.442-s2.0-85063987237Q3WOS:000460758200032Q4