    Synthesis and characterization of a new eco-friendly dopamine derivative schiff base as an effective corrosion inhibitor for mild steel in acidic environment
    (Taylor & Francis Ltd, 2024) Ozkir, Demet; Bay, Yasemin
    The natural corrosion inhibitor behaviour of a newly synthesized dopamine derivative Schiff base (4-DBAB) has been inspected on mild steel in aggressive 1 M HCl using linear polarization, electrochemical impedance spectroscopy and potentiodynamic polarization techniques. The Schiff base was synthesized by eco-friendly pathway. Characterization of the synthesized new non-toxic inhibitor was performed using FT-IR and 1H-NMR spectroscopy techniques. The anti-corrosive efficiencies at optimum concentration of 4-DBAB inhibitor was 87.4% after 1 h and 98.4% after 120 h by impedance technique in acidic solution. The potential of zero charge of mild steel was also determined to elucidate the inhibition mechanism in the presence of the highest 4-DBAB solution. The atomic force microscopy and field emission scanning electron microscopy researches performed on surface morphology to provide additional support on the interaction between the mild steel surface and 4-DBAB molecules. Adsorption behaviour of the inhibitor was also studied at different durations by experimental inhibition results and showed the Langmuir isotherm involving chemisorption.HighlightsA new dopamine-derived Schiff base (4-DBAB) with natural and environmentally friendly corrosion inhibition properties was synthesized. (Synthesis of eco-friendly compound).4-DBAB demonstrated a high anti-corrosive efficiency after 120 hours in aggressive 1M HCl, as determined by impedance technique. (Exceptional corrosion inhibition).The determination of the potential of zero charge of mild steel provided insights into the inhibition mechanism in the presence of the highest 4-DBAB solution. (Mechanism elucidation).AFM and FE-SEM studies on surface morphology supported the interaction between the mild steel and 4-DBAB molecules, affirming its corrosion inhibition properties. (Surface interaction analysis).
  • Küçük Resim Yok
    Öğe
    Yeni tip korozyon inhibitörü sentezi, karakterizasyonu ve asidik ortamda yumuşak çeliğin korunması üzerine etkilerinin incelenmesi
    (Niğde Ömer Halisdemir Üniversitesi, 2023) Bay, Yasemin; Özkır, Demet
    Bu tez çalışmasında, yeşil bir korozyon inhibitörü olarak kondensasyon tepkimesi ile literatüre göre yeni bir Schiff bazı sentezlenmiş ve bileşiğin yapısı FT-IR ve 1H-NMR analizleriyle aydınlatılmıştır. Bu yeni tip Schiff bazının uygulanabilirliğini test etmek amacıyla, 1,0 M HCl çözeltisindeki yumuşak çeliğin korozyon davranışına inhibitör etkisi bazı elektrokimyasal yöntemlerle araştırılmıştır. Ölçümlerde inhibitör olarak 1,0x10–5 M–1,0x10–3 M Schiff bazı içeren ve içermeyen 1,0 M HCl çözeltileri kullanılmıştır. Bu çözeltilerle 298 K'de bir saat daldırma süresi sonunda EIS, LPR ve potansiyodinamik polarizasyon ölçümleri yapılmıştır. Yeni Schiff bazının hem kısa hem de uzun daldırma sürelerinde etkin olduğu görülmüştür. Hidroklorik asitli ortamdaki yumuşak çeliğin korozyonunu, yeşil inhibitör olarak sentezlenen Schiff bazının önleme etkisi ayrıca FE-SEM ve AFM yüzey analiz teknikleriyle incelenmiştir. Yüzey analizleri sonucunda, elektrot yüzeyinde korozyona karşı koruyucu bir film tabakası oluştuğu net bir şekilde gözlenmiştir. Hem elektrokimyasal deney sonuçları hem de yüzey analiz bulguları birbiriyle son derece uyumlu olmuştur. Bu çalışma ile sentezlenen yeni Schiff bazı, asidik ortamdaki yumuşak çelik için başarılı bir inhibitör olarak uygulanmıştır.