    Catholuminescence properties of rare earth doped CaSnO3 phosphor
    (PERGAMON-ELSEVIER SCIENCE LTD, 2015) Canimoglu, A.; Garcia-Guinea, J.; Karabulut, Y.; Ayvacikli, M.; Jorge, A.; Can, N.
    The present study describes cathodoluminescence (CL) properties of CaSnO3 phosphors doped with Eu3+, Tb3+ and Dy3+ synthesized by a solid-state method. X-ray diffraction (XRD) patterns confirm that CaSnO3 sintered at 1200 degrees C exhibits orthorhombic structure. The evidence and rationale for two strong broad emission bands appeared at 360 and 780 nm for undoped CaSnO3 are presented. The CL measurements exhibit that the 4f-4f emissions from D-5(4) -> F-7(5) (490 nm), D-5(4) -> F-7(5) (544 nm), D-5(4) -> F-7(4) (586 nm) and D-5(4) -> F-7(3) (622 nm), assigned to possible transitions of Tb3+ ions are seen. The strongest one, observed at 544 nm, due to its probability of both magnetic and electric transitions make the sample emission green. Emissions at 480, 574, 662 and 755 nm were detected for the CaSnO3:Dy3+ and attributed to the transitions from the F-4(9/2) to various energy levels H-6(15/2), H-6(13/2), H-6(11/2) and H-6(9/2)+F-6(11/12) of Dy3+, respectively. CL spectra of Eu doped CaSnO3 reveal that there is a strong emission peak appeared at 615 am due to the electric dipole transition D-5(0) -> F-7(2) (red). Finally, our results show that the rare earth doped CaSnO3 have remarkable potential for applications as optical materials since it exhibits efficient and sharp emission due to rare earth ions. (C) 2015 Elsevier Ltd. All rights reserved.
  • Küçük Resim Yok
    Öğe
    Luminescent, Structural, and Thermal Properties of the Unusual "Anatolian" Diaspore (Zultanite) from Turkey
    (TAYLOR & FRANCIS INC, 2014) Canimoglu, A.; Garcia-Guinea, J.; Correcher, V.; Karabulut, Y.; Tuncer, Y.; Can, N.
    Results are presented for the cathodoluminescence (CL) probe of an environmental scanning electron microscopy (ESEM) with an energy-dispersive spectrometry analyzer (EDS), thermoluminescence (TL), thermo X-ray diffraction in situ (TXRD), and simultaneous differential thermal analysis and thermogravimetric analysis (DTA/TGA) techniques of gem-quality zultanite samples collected from the Mugla region of southwest Turkey. Micro-Raman measurements were also performed on different zultanite orientations and preheated aliquots to study the spectral phase transition diaspore-corundum also detected by the other thermal techniques in the 450 degrees C-500 degrees C thermal range. The thermal phenomena of TL are synchronous with this dehydroxylation process, involving consecutive breaking-linking bonds of Al-O, Cr-O, Fe-O, Al-OH, Cr-OH, and Fe-OH, including the formation of hydrolyzed ions such , and and redox reactions. Assuming that zultanite oxygen atoms are distributed as a hexagonal close packed layer, the experimental spectrum CL of zultanite is characteristic of the E-2 ->(4)A(2) transitions of substitutional Cr3+ luminescent centers in positions of Al3+ in sixfold coordination.
  • Küçük Resim Yok
    Öğe
    Solid state synthesis, characterization and optical properties of Tb doped SrSnO3 phosphor
    (ELSEVIER SCIENCE SA, 2013) Kotan, Z.; Ayvacikli, M.; Karabulut, Y.; Garcia-Guinea, J.; Tormo, L.; Canimoglu, A.; Can, N.
    In the present study, the structural and optical properties of SrSnO3 doped with Tb ions are reported. Novel SrSnO3:Tb3+ phosphors were conventionally synthesized using a solid state reaction process under a mildly reduced atmosphere (5% H-2 and 95% N-2). The crystal structures, morphologies and optical properties of the resultant materials have been characterised by experimental techniques such as X-ray Diffraction (XRD), Raman spectroscopy (RS), Photoluminescence (PL), Radioluminescence (RL) and Cathodoluminescence coupled to an ESEM (ESEM-CL). The new phosphor material has good crystallization without any impurity phases, which matches with the standard JCPDS files (No. 22-1442) from XRD analysis. The PL, RL and CL measurements taken at room temperature showed that the transitions of D-5(4) to F-7(J) (j = 6, 5, 4, 3) corresponding to the typical 4f -> 4f dipole forbidden intra-configurational transitions of Tb3+ are largely independent of the host material. The green emissions of the D-5(4) -> F-7(5) magnetic dipole transition at similar to 540 nm are predominant for three types of luminescence. PL emission spectra recorded in the temperature range from 10 K to 300 K were influenced by temperature. We report anomalies in the PL spectra of SrSnO3:Tb3+ compatible with a structural phase transition at 260 K while simultaneously exciting and cooling the sample. This work clearly confirms the existence of a phase transition discovered by Singh et al. in SrSnO3 at 270 K. (C) 2013 Elsevier B.V. All rights reserved.