Interflake spacings and undercoolings in Al-Si irregular eutectic alloy

Küçük Resim Yok

Tarih

2004

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

ELSEVIER SCIENCE SA

Erişim Hakkı

info:eu-repo/semantics/closedAccess

Özet

Aluminium-silicon irregular eutectic alloy was melted in a graphite crucible in vacuum. This alloy was directionally solidified at a constant growth rate, V (8.3 mum/s) and at different temperature gradients, G (2.0-7.8 K/mm) and also with a constant G (7.8 K/mm) and different V (8.3-498.7 mum/s) in the Bridgman type directional solidification furnace. The interflake spacings, lambda(i), were measured from both transverse and longitudinal sections of the specimens. The relationships between interflake spacings, lambda(i) and solidification parameters V and G were obtained by linear regression analysis method. The variations of interflake spacings, lambda(i) with V, G and undercoolings, DeltaT(i), were investigated and the relationships between them were examined. Operating parameters phi and eta which reflect the spacing adjustment mechanism were obtained. lambda(i)(2)V, lambda(i) DeltaT(i), DeltaT(i)V(-a), lambda(i)(3)G and DeltaT(i)G(-b) values were determined by using lambda(i), V, G and DeltaT(i), values. The results obtained in this work have been compared with the eutectic theory and previous experimental results. (C) 2003 Elsevier B.V. All rights reserved.

Açıklama

Anahtar Kelimeler

Al-Si eutectic alloy, directional solidification, microstructure, operating parameters, uridercooling

Kaynak

MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING

WoS Q Değeri

Q2

Scopus Q Değeri

Q1

Cilt

369

Sayı

45323

Künye