dc.description.abstractStar crack defects encountered during the continuous casting of slab are elucidated in the current article. Trials were carried out to obtain basic information on the behavior of the star cracks under same casting conditions for different grade materials. It is important that star cracks form in the mold, and increase later in the casting process during the straightening. Star crack defects are clearly seen when using copper-based molds. The influences of steel carbon content, material grades, and mold type have been discussed. It is believed that defects in continuously cast products are minimized while using a nickel-coated mold wall in casting.
dc.identifier.doi10.1007/s11663-013-9821-0
dc.identifier.endpage710
dc.identifier.issn1073-5615
dc.identifier.issn1543-1916
dc.identifier.issue3
dc.identifier.scopus2-s2.0-84877743824
dc.identifier.scopusqualityQ1
dc.identifier.startpage706
dc.identifier.urihttps://dx.doi.org/10.1007/s11663-013-9821-0
dc.identifier.urihttps://hdl.handle.net/11480/4400
dc.identifier.volume44
dc.identifier.wosWOS:000318736900019
dc.identifier.wosqualityQ2
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.institutionauthor[0-Belirlenecek]
dc.language.isoen
dc.publisherSPRINGER
dc.relation.ispartofMETALLURGICAL AND MATERIALS TRANSACTIONS B-PROCESS METALLURGY AND MATERIALS PROCESSING SCIENCE
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.titleEffects of Nickel Coating of Mold Plates on Star Crack Defects
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu