Improvement of Wear Resistance in Toothed Harrows Coated with HVOF and PVD Methods
Küçük Resim Yok
Tarih
2023
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Tarbiat Modares Univ
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Surfaces of the toothed harrow were improved by using different coating materials and methods. Four different coating methods and special alloy powders were used as coating materials. TiCN was applied with PVD, and the WC-Ni-Co-Cr-Si-Fe-B powder mixture was applied with HVOF. The coating thicknesses was 2 mu m and 5 mu m in PVD, 500 mu m in the HVOF, and 500+2 mu m in the application where HVOF+PVD were used together. The wear trials were carried out in the laboratory, at a 50 km distance, in a double-speed trial pattern that converted circular motion to linear motion. The trial model was used to simulate the wear that occurs under real operating conditions in the soil. As a result of the wear trials carried out under the same operating conditions, a total material loss of 3.99 g occurred in the control (uncoated) harrow, the wear resistance increased, and less material loss was observed in the coated harrows. The sample coated with the PVD method had the lowest value with a material loss of 0.14 g. Material loss for other coated samples PVD-5 mu, HVOF-500 mu, and PVD-2 mu+HVOF-500 mu was 0.19, 0.28, and 0.18 g, respectively. When the amount of wear in the uncoated sample was 100%, the proportional loss in PVD-2 mu, PVD- 5 mu, HVOF-500 mu, and PVD-2 mu+HVOF-500 mu coated samples was calculated as 3.41, 4.85, 7.16, and 4.57%, respectively.
Açıklama
Anahtar Kelimeler
Agricultural Machinery, Abrasion, Material loss, Coating
Kaynak
Journal of Agricultural Science and Technology
WoS Q Değeri
Q2
Scopus Q Değeri
Q3
Cilt
25
Sayı
1