The Dependence of Lamellar Spacings and Microhardness on the Growth Rate in the Directionally Solidified Bi-43 wt.% Sn Alloy at a Constant Temperature Gradient
Küçük Resim Yok
Tarih
2009
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
KOREAN INST METALS MATERIALS
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Bi-43 wt.% Sn eutectic samples were directionally solidified upward with five different growth rates (V = 8.3-164.8 mu m/s) at a constant temperature gradient (G = 3.55 K/mm) in a Bridgman type directional solidification furnace. The lamellar spacings (lambda) and microhardness values (H(V)) were measured from the quenched samples; the directionally solidified Bi-43 wt.% Sn eutectic alloy and the minimum undercoolings (Delta T) were determined from the Jackson-Hunt eutectic theory. The dependency of lamellar spacings (lambda), microhardness (H(V)) and undercooling (Delta T) on the growth rate (V) were analyzed. According to these results, it has been found that the value of lambda decreases with the increasing value of V and that the values of H(V) and Delta T increase for a constant G. The values of lambda(2)V, lambda Delta T and Delta T V(-0.5) were determined by using the values of lambda, Delta T and V. The results obtained in the present work have been compared with those predicted by the Jackson-Hunt eutectic theory and with similar experimental results.
Açıklama
Anahtar Kelimeler
metals and alloys, directional solidification, mechanical properties, microstructure
Kaynak
METALS AND MATERIALS INTERNATIONAL
WoS Q Değeri
Q1
Scopus Q Değeri
Q1
Cilt
15
Sayı
5