Directional solidification of aluminium - copper alloys
Küçük Resim Yok
Tarih
2002
Yazarlar
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
ELSEVIER SCIENCE SA
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Directional solidification experiments have been carried out on different Al-Cu alloys as a function of solidification parameters, temperature gradient G, growth rate V, and composition C-0. The specimens were solidified under steady state conditions with a constant temperature gradient (7.4 K mm(-1)) at a wide range of growth rates (9-490 m s(-1)) and with a constant growth rate of 9.5 mum s(-1) at a wide range of temperature gradients (1.0-7.4 K mm(-1)). Microstructural parameters, the primary dendrite arm spacing lambda(1), secondary dendrite arm spacing lambda(2), dendrite tip radius R, mushy zone depth d were measured and expressed as functions of solidification parameters, G, V and C-0 by using a linear regression analysis. The results were in good agreement with previous experimental work and current theoretical models suggested for dendritic growth. (C) 2002 Elsevier Science B.V. All rights reserved.
Açıklama
Anahtar Kelimeler
Al-Cu alloys, directional solidification, primary dendrite arm spacing, secondary dendrite arm spacing, dendrite tip radius, mushy zone depth
Kaynak
MATERIALS SCIENCE AND ENGINEERING A-STRUCTURAL MATERIALS PROPERTIES MICROSTRUCTURE AND PROCESSING