Characterization of a Directionally Solidified Sn-Pb-Sb Ternary Eutectic Alloy

Basit Öğe Kaydı
dc.contributor.authorCadirli, E.
dc.contributor.authorSahin, M.
dc.contributor.authorTurgut, Y.
dc.date.accessioned2019-08-01T13:38:39Z
dc.date.available2019-08-01T13:38:39Z
dc.date.issued2015
dc.departmentNiğde ÖHÜ
dc.description.abstractA Sn-40.5wt%Pb-2.6wt%Sb ternary eutectic alloy was prepared using a vacuum melting furnace and a casting furnace. The samples were directionally solidified at a constant growth rate (V = 16.5 mu m/s) under different temperature gradients (G = 1.05-3.88 K/mm) and at a constant temperature gradient (G = 3.88 K/mm) under different growth rates (V = 8.3-498 mu m/s). The effects of G and V on lamellar spacing (lambda), microhardness (HV), and ultimate tensile strength (sigma) were determined. The lamellar spacing and microhardness were measured from both longitudinal and transverse sections of the sample. The relationships between solidification parameters (G, V), microstructure parameters (lambda(L), lambda(T)), and mechanical properties (HV, sigma) were determined from linear regression analysis. It was found that the microhardness and tensile strength increase with increasing G and V as well as with decreasing lambda.
dc.description.sponsorshipNigde University Scientific Research Project Unit
dc.description.sponsorshipThis project was supported by the Nigde University Scientific Research Project Unit under contract No: FEB 2011/23. The authors thank for their financial support.
dc.identifier.doi10.1007/s13632-015-0211-7
dc.identifier.endpage297
dc.identifier.issn2192-9262
dc.identifier.issn2192-9270
dc.identifier.issue4
dc.identifier.scopus2-s2.0-84939199862
dc.identifier.scopusqualityQ2
dc.identifier.startpage286
dc.identifier.urihttps://dx.doi.org/10.1007/s13632-015-0211-7
dc.identifier.urihttps://hdl.handle.net/11480/3901
dc.identifier.volume4
dc.identifier.wosWOS:000218798400003
dc.identifier.wosqualityN/A
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.institutionauthor[0-Belirlenecek]
dc.language.isoen
dc.publisherSPRINGER
dc.relation.ispartofMETALLOGRAPHY MICROSTRUCTURE AND ANALYSIS
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.subjectDirectional solidification
dc.subjectMicrostructure
dc.subjectMicrohardness
dc.subjectTensile strength
dc.titleCharacterization of a Directionally Solidified Sn-Pb-Sb Ternary Eutectic Alloy
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu