Dendritic solidification and characterization of a succinonitrile-acetone alloy

Basit Öğe Kaydı
dc.contributor.authorUstun, Erkan
dc.contributor.authorCadirli, Emin
dc.contributor.authorKaya, Hasan
dc.date.accessioned2019-08-01T13:38:39Z
dc.date.available2019-08-01T13:38:39Z
dc.date.issued2006
dc.departmentNiğde ÖHÜ
dc.descriptionSymposium on Low Friction Coatings on Glass and Ceramics -- APR, 2005 -- Baltimore, MD
dc.description.abstractA succinonitrile (SCN)-3.6 wt% acetone (ACE) alloy was unidirectionally solidified with a constant temperature gradient G = 5.7 K mm(-1) in the growth rate ranges V = 6.5 - 113 mu m s(-1) and a constant growth rate V = 6.5 mu m s(-1) in the temperature gradient ranges G = 3.5-5.7 K mm(-1). The primary dendrite arm spacings, secondary dendrite arm spacings, dendrite tip radius and mushy zone depth were measured as a function of growth rate and temperature gradient. Theoretical models for the dendrite arm spacing and tip radius have been compared with the experimental observations, and a comparison of our results with the current theoretical models and previous experimental results has also been made. The stability constant (s) for this alloy system was measured and this result was compared with various similar organic transparent alloys.
dc.description.sponsorshipNatl Sci Fdn, NIH
dc.identifier.doi10.1088/0953-8984/18/32/026
dc.identifier.endpage7839
dc.identifier.issn0953-8984
dc.identifier.issue32
dc.identifier.pmid21690889
dc.identifier.scopus2-s2.0-33746662282
dc.identifier.scopusqualityQ2
dc.identifier.startpage7825
dc.identifier.urihttps://dx.doi.org/10.1088/0953-8984/18/32/026
dc.identifier.urihttps://hdl.handle.net/11480/5493
dc.identifier.volume18
dc.identifier.wosWOS:000239558500031
dc.identifier.wosqualityQ2
dc.indekslendigikaynakWeb of Science
dc.indekslendigikaynakScopus
dc.indekslendigikaynakPubMed
dc.institutionauthor[0-Belirlenecek]
dc.language.isoen
dc.publisherIOP PUBLISHING LTD
dc.relation.ispartofJOURNAL OF PHYSICS-CONDENSED MATTER
dc.relation.publicationcategoryMakale - Uluslararası Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/closedAccess
dc.titleDendritic solidification and characterization of a succinonitrile-acetone alloy
dc.typeArticle

Dosyalar

Koleksiyon

WoS İndeksli Yayınlar Koleksiyonu
PubMed İndeksli Yayın Koleksiyonu
Scopus İndeksli Yayınlar Koleksiyonu