Yazar "Güneş, Muhammet" seçeneğine göre listele
Listeleniyor 1 - 7 / 7
Sayfa Başına Sonuç
Sıralama seçenekleri
Öğe Basic durability properties of standard mortars produced with recycled glass powder(Niğde Ömer Halisdemir Üniversitesi, 2019) Yücel, Hasan Erhan; Öz, Hatice Öznur; Güneş, Muhammet; Kaya, YasinThis research presents the basic durability properties of standard mortars (SMs) produced with recycled glass powder (RGP). In this study, six SM mixtures as well as control mixture were designed with constant water/binder (w/b) ratio of 0.48. In the mixtures, cement was replaced by RGP partially ranging from 0% to 30% by steps of 5% increment. Firstly, the slump flow diameters of SMs are determined and then the basic durability properties of SMs were observed in terms of water sorptivity, rapid chloride permeability and gas permeability. Finally, the relations between basic durability properties were determined for 7 and 28 days. According to test results, it is found that the RGP increased the workability of SMs. In addition, the highest durability performance was determined for SM incorporating 5% RGP. However, basic durability performances of SMs incorporating 10% RGP were also identified as higher than that of the control mixture. When the correlation coefficients are considered, strong relationships between durability properties are determined.Öğe DOĞAL VOLLASTONİTİN YÜKSEK PERFORMANSLI HARÇLAR ÜZERİNEETKİLERİ(2020) Öz, Hatice; Yücel, Hasan; Güneş, Muhammet; Malkoç, BeytullahBu çalışma kapsamında Finlandiya’dan temin edilen doğal vollastonitin, yüksek performanslı harcın (YPH) dayanım ve durabilite özellikleri üzerindeki etkileri araştırılmıştır. YPH üretim aşamasında su/bağlayıcı oranı sabit tutularak, vollastonit minerali %3, %6, %9, %12 ve %15 oranlarında karışıma eklenmiştir. Ayrıca yüksek oranda su azaltıcı katkı maddesi (SA) vasıtasıyla karışımın işlenebilirliği sağlanmıştır. Basınç, eğilme ve ultrasonik titreşim hızı testleri 3., 7., 28. ve 90. günlerde yapılırken, kılcal su geçirimliliği ve gaz geçirimliliği deneyleri 28. ve 90. günde uygulanmıştır. Bu deneylerden elde edilen sonuçlara göre, %3 vollastonit içeren karışımda tüm deneyler için performansta iyileşme gözlenmiştir. %6 vollastonit içeriğine sahip karışımda ise kontrol harcına oranla daha iyi sonuçlar elde edilirken, %3 vollastonit içeren karışıma göre performansta azalmalar gözlenmiştir.Öğe Farklı tasarım ve kür parametreleri ile geliştirilen tasarlanmış geopolimer kompozitlerin özellikleri üzerine sentetik vollastonit mikrofiberlerin etkileri(Niğde Ömer Halisdemir Üniversitesi, 2023) Güneş, Muhammet; Öz, Hatice ÖznurDört aşamada gerçekleştirilen bu tez çalışmasının ilk aşamasında, SVM-I ve SVM-II kodlu sentetik vollastonit mikrofiberler (SVM'ler) geliştirilmiştir. SVM-I; doğal kaynaklardan üretilirken, SVM-II; farklı atık malzemeler ve tasarım parametreleri ile geliştirilen SVM'ler arasından seçilmiştir. İkinci aşamada ise standart olarak M45 kodu ile bilinen tasarlanmış çimento esaslı kompozit (M45-ECC) ile benzer ''taşıma gücü ve deformasyon kapasitesine'' ulaşabilecek bir tasarlanmış geopolimer kompozit (EGC) geliştirilmeye çalışılmıştır. Bu amaçla, farklı tasarım ve kür parametreleri ile uçucu kül (UK) ve uçucu kül+cüruf (UK+C) esaslı EGC'ler geliştirilmiştir. EGC'ler, taze ve reolojik özellikleri M45-ECC'ye benzer olacak şekilde tasarlanmıştır. Ayrıca, M45-ECC ve EGC'lerin mekanik ve mikroyapısal özellikleri araştırılmıştır. Geliştirilen UK/UK+C esaslı EGC karışımları arasından bir UK+C esaslı EGC karışımı seçilmiştir. Üçüncü aşamada, SVM-I ve SVM-II vollastonitleri UK yerine %3, %6 ve %9 oranlarında kullanılmıştır. Mekanik testler ve mikroyapısal analizler, SVM-I mineralinin UK+C esaslı EGC'lerin performansını daha etkili bir şekilde geliştirdiği göstermiştir. Bu nedenle, dördüncü ve son aşamada, M45-ECC ve SVM-I içeren UK+C esaslı EGC'lerin geçirimlilik, durabilite ve boyutsal stabilite özellikleri incelenmiştir. Sonuçlara göre, %6 SVM-I içeriği optimum kullanım oranı olarak belirlenmiştir.Öğe Mechanical and microstructural properties of cement mortars developed with different curing conditions and design parameters(2022) Güneş, Muhammet; Yücel, Hasan; Öz, HaticeThe aim of this study is the investigation of microstructural effects on cement mortars (CMs) of four different parameters as cement dosage, water/cement ratio, pozzolanic material and curing effect. To achieve the purpose of this study, SEM/EDX, XRD, FTIR and TGA/DTA analysis were performed. A total of 18 mixtures were produced and exposed to water curing (WC) and air curing (AC). In the design of these mixtures, three different cement dosages as 360, 400 and 450 kg/m3 and three different water/cement ratios as 0.40, 0.45 and 0.50 were used. Silica fume (SF) was preferred to observe the effect on microstructural properties clearly of pozzolanic material. In addition, super plasticizer (SP) was utilized in all mixtures and kept constant as 12 kg/m3. The compressive strength, flexural strength and ultrasonic pulse velocity (UPV) of these mixtures were determined at 28 and 90 days. Eight mixtures were chosen to observe the effect of four different parameters in a microstructural sense. XRD, SEM/EDX, FTIR and TGA/DTA analyses were applied to these mixtures. It can be said that microstructural analyses supported the findings obtained from mechanical tests.Öğe Tasarlanmış çimento esaslı kompozit ile uçucu kül ve cüruf esaslı tasarlanmış geopolimer kompozitlerin mekanik ve mikroyapısal özellikleri(2023) Öz, Hatice; Güneş, MuhammetBu çalışmada, literatürde M45 kodu ile bilinen standart tasarlanmış çimento esaslı kompozite (ECC) benzer taşıma gücü ve deformasyon kapasitesine sahip bir uçucu kül+yüksek fırın cürufu (UK+YFC) esaslı tasarlanmış geopolimer kompozit (EGC) karışımının geliştirilmesi amaçlanmıştır. Bu amaçla ECC’nin yanı sıra farklı oranlarda UK ve YFC içeren iki farklı EGC karışımı geliştirilmiştir. Üretilen bu üç karışımın taze ve reolojik özelliklerinin yanı sıra basınç dayanımı, elastisite modülü, hava kurusu birim hacim ağırlığı, yapısal verimliliği, ultrasonik titreşim hızı (UTH), kırılma tokluğu ve eğilme performansı 7. ve 28. günlerde belirlenmiştir. Sonuçta, ECC’den çok daha yüksek basınç dayanımına ve sünekliğe sahip bir EGC karışımı elde edilmiştir. Ayrıca, artan YFC içeriğinin mekanik dayanımı ve tokluğu artırdığı ancak, sünekliği azalttığı tespit edimiştir. Bu durumun nedenleri XRD, TGA/DTA ve FTIR analizleri ile mikroyapısal olarak araştırılmıştır.Öğe Türkiye’de Atık Malzemeden Yapılmış Kendiliğinden Yerleşen Harç Üretiminin Yaşam Döngüsü Analizi(Niğde Üniversitesi, 2019) Demirel, Sevgi; Öz, Hatice Öznur; Çiner, Fehiman; Güneş, MuhammetYaşam döngüsü değerlendirmesi (YDD), binaların ve inşaat malzemelerinin çevresel performansını analiz etmek için kullanılan bir yöntemdir. Betonda bağlayıcı malzeme olarak kullanılan çimento, üretimi esnasında sera gazı ortaya çıkarmaktadır. Dünya genelinde, toplam CO2 emisyonunun yaklaşık olarak %5-8’si çimento üretiminden kaynaklanmaktadır. Sera gazı emisyonlarının azaltılması amacıyla, çimentonun atık malzemelerle (uçucu kül, atık cam ve yüksek fırın cürufu vb.) ikame edilmesi giderek önem kazanmaktadır. Bu çalışmada, beşikten-kapıya (cradle to gate) yaklaşımı ile atık malzeme (camPET ve uçucu kül) kullanımının kendiliğinden yerleşen harç üretiminin çevresel performansı üzerindeki etkileri ortaya konulmuştur.Öğe Vollastonit katkılı yüksek performanslı harçların mekanik ve durabilite özellikleri(Niğde Ömer Halisdemir Üniversitesi / Fen Bilimleri Enstitüsü, 2018) Güneş, Muhammet; Öz, Hatice ÖznurBu tezde, vollastonit katkılı yüksek performanslı harcın (YPH) taze, mekanik ve durabilite özellikleri deneysel olarak incelenmiştir. İlk aşamada vollastonit mineralinin literatür çalışmaları dışında belirlenen özel bir yöntemle sentetik olarak üretimi yapılmış, ikinci aşamada ise sentetik vollastonit YPH üretiminde kullanılmıştır. Vollastonit katkılı yüksek performanslı harç (VYPH) üretimi 0.33 sabit su/bağlayıcı (çimento+vollastonit) oranıyla, 132±10 mm sabit bir yayılma çapıyla ve yüksek oranda su azaltıcı katkı (süper akışkanlaştırıcı) kullanılarak gerçekleştirilmiştir. İlk olarak, kontrol harcı sabit su/bağlayıcı oranı ile üretilmiş ve daha sonra sentetik vollastonit sırasıyla, %3, %6, %9 ve %12 oranlarında her defasında çimentonun yerine ikinci bir bağlayıcı malzeme olarak ikame edilmiştir. Üretilen harçların sarsma tablasında yayılma çapı ölçülmüştür. Sonrasında, harçlara basınç ve eğilme testlerinin yanı sıra ultrasonik titreşim hızı, kılcal su geçirimliliği ve hızlı klor geçirimliliği testleri 28. ve 90. günlerde uygulanmıştır. Deney sonuçlarına göre, vollastonit miktarının artmasıyla yayılma çapı giderek azalmış, mekanik ve durabilite özellikleri %9’a kadar iyileşmiştir.
