    Effect of Temperature Gradient and Growth Velocity on Microstructure and Mechanical Properties on Zn-7Al-3Cu Ternary Eutectic Alloy
    (Springer International Publishing Ag, 2021) Yilmazer, I.; Cadirli, E.
    In the present work, microstructure and mechanical properties of Zn-7Al-3Cu (wt%) ternary alloy are investigated depending on the temperature gradient and growth velocity. The alloy was prepared in the designated composition in a vacuum melting and casting furnace and then filled into the graphite sample moulds. The samples were directional solidified with various temperature gradients (6.7-10.7 K/mm) at a constant growth velocity (16.4 mu m/s) and with various growth velocities (8.3-166.0 mu m/s) at a constant temperature gradient (10.7 K/mm) in a Bridgman-type furnace. Microstructural images of solidified samples were taken with light microscope and scanning electron microscope. Eutectic spacings were measured from these images. Microhardness, ultimate tensile strength, yield strength and modulus elasticity values of each sample produced at various solidification parameters were also measured. The effect of temperature gradient and growth velocity on the eutectic spacing, microhardness, ultimate tensile strength, yield strength and modulus elasticity was determined using linear regression analysis. While the microhardness, ultimate tensile strength, yield strength and modulus elasticity values increased with increasing temperature gradient and growth velocity values or decreasing eutectic spacing, the elongation values decreased. Fractographic results show that the type of fracture is brittle.
  • Küçük Resim Yok
    Öğe
    Physical Properties of Directionally Solidified Al-1.9Mn-5Fe Alloy (Nov, 10.1007/s11665-020-05253-3, 2020)
    (Springer, 2021) Yilmazer, I.; Cadirli, E.; Kaya, H.; Buyuk, U.
    [Abstract Not Available]
  • Küçük Resim Yok
    Öğe
    Temperature-dependence of electrical resistivity of Cd-Sn, Bi-Sn, and Al-Si eutectic and Al-3wt.%Si hypoeutectic alloys
    (SPRINGER, 2006) Cadirli, E.; Kaya, H.; Guemues, A.; Yilmazer, I.
    Cd-Sn, Bi-Cd, and Al-Si eutectic and Al-3wt.%Si hypoeutectic alloys of high-purity (99.99%) metals were produced in a vacuum atmosphere. Current-voltage (I-V) characteristics of these specimens were measured at various temperatures between 100 and 475 K. The electrical resistivity (p) and temperature coefficient (alpha) for each specimen, depending on the temperature, were calculated using results obtained from the I-V measurements. The electrical resistivities and the residual resistivity of the specimens increase with increasing temperature for each alloy system. These results are compared with literature results.