Comparative studies on thermoluminescence characteristics of non-doped Mg2SiO4 prepared via a solid-state reaction technique and wet-chemical method: An unusual heating rate dependence

Küçük Resim Yok

Tarih

2019

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Elsevier Science Sa

Erişim Hakkı

info:eu-repo/semantics/closedAccess

Özet

Magnesium orthosilicate (Mg2SiO4) was synthesized via a traditional solid-state reaction and a wet chemical route. This study primarily reported the thermoluminescence (TL) behavior of Mg2SiO4 host. X-ray diffraction pattern revealed that Mg2SiO4 exhibits orthorhombic structure matched with JCPDS card 900-6398. Dose response, reproducibility and trap parameters of TL glow curves were evaluated to clearly reveal TL features. Two TL glow peaks situated at 81 degrees C and 192 degrees C were monitored at a heating rate of 2 degrees Cs-1. We observed anomalous heating rate effect for the peak centered at 192 degrees C whilst TL intensity of the peak at 81 degrees C decreases with elevating heating rate. Trap depths of the electrons within the trap centers were found to be 1.04 +/- 0.01eV and 1.37 +/- 0.01eV for both methods using peak shape (PS) method. Distribution of trap centers was examined using the T-max - T-stop method and this case indicated that the glow curves consist of single TL peaks. The intensity of TL glow curves exhibited a good linear dose response under total area up to 20 Gy. A comparison of the two preparation techniques revealed that TL characteristics of this phosphor are partly dependent and Mg2SiO4 could be a promising material for dosimetric application. (C) 2019 Elsevier B.V. All rights reserved.

Açıklama

Anahtar Kelimeler

Mg2SiO4, XRD, Thermoluminescence, Heating rate, Mg2SiO4, XRD, Thermoluminescence, Heating rate

Kaynak

Journal of Alloys and Compounds

WoS Q Değeri

Q1

Scopus Q Değeri

Q1

Cilt

795

Sayı

Künye