FARKLI PUZOLANLARLA ÜRETİLMİŞ ÇİMENTOLARIN DAYANIM GELİŞİMİNİN YAPAY SİNİR AĞLARIYLA TAHMİNİ
Küçük Resim Yok
Tarih
2009
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
Erişim Hakkı
info:eu-repo/semantics/openAccess
Özet
Bu çalışma, çimento üretiminde kullanılan mineral katkılarda en uygun kullanım oranının belirlenmesi için yapılmıştır. Laboratuvarda farklı kaynaklardan sağlanan doğal zeolit, tras, volkanik tüf, uçucu kül ve yüksek fırın cürufu katkıları, çimento üretiminde klinker yerine %10, 20, 30, 35, 40 ve 45 oranlarında kullanılmıştır. Çimentolar üzerinde yapılan 2, 7, 28 ve 180 günlük basınç dayanımı deneyleriyle dayanım gelişimi belirlenmiştir. Daha sonra deneysel çalışmadan elde edilen veriler kullanılarak yapay sinir ağı (YSA) yönteminde model geliştirilmiştir.
This study is based on the determination of optimum usage of mineral additives as supplementary cementing material for blended cement production. For this purpose, blended cements were produced under laboratory conditions with natural zeolite, trass, volcanic tuff, fly ash and ground granulated blast furnace slag at 10, 20, 30, 40 and 45% clinker replacement ratios. Strength development of the cements was determined with compressive strength tests performed at 2, 7, 28 and 180 days. Experimental results were also obtained by building models according to artificial neural network (ANN) system.
This study is based on the determination of optimum usage of mineral additives as supplementary cementing material for blended cement production. For this purpose, blended cements were produced under laboratory conditions with natural zeolite, trass, volcanic tuff, fly ash and ground granulated blast furnace slag at 10, 20, 30, 40 and 45% clinker replacement ratios. Strength development of the cements was determined with compressive strength tests performed at 2, 7, 28 and 180 days. Experimental results were also obtained by building models according to artificial neural network (ANN) system.
Açıklama
Anahtar Kelimeler
Mimarlık
Kaynak
Eskişehir Osmangazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi
WoS Q Değeri
Scopus Q Değeri
Cilt
22
Sayı
3 özel sayı