Vollastonit katkılı kendiliğinden yerleşen geopolimerin taze ve mekanik özelliklerinin deneysel olarak incelenmesi

Basit Öğe Kaydı
dc.contributor.advisorÖz, Hatice Öznur
dc.contributor.authorTecimer, Dilara
dc.date.accessioned2024-11-04T20:07:44Z
dc.date.available2024-11-04T20:07:44Z
dc.date.issued2021
dc.departmentNiğde ÖHÜ, Fen Bilimleri Enstitüsü, İnşaat Mühendisliği Ana Bilim Dalı
dc.descriptionFen Bilimleri Enstitüsü, İnşaat Mühendisliği Ana Bilim Dalı
dc.description.abstractBu tez çalışmasında, vollastonit katkılı kendiliğinden yerleşen geopolimer harçların (KYG) farklı kür sıcaklıklarında taze, mekanik ve fiziksel özellikleri incelenmiştir. Bağlayıcı malzeme olarak kullanılan F sınıfı uçucu kül, sodyum silikat ve sodyum hidroksit çözeltileri ile aktifleştirilerek KYG tasarımı yapılmıştır. Çalışmanın ilk aşamasında sentetik vollastonit minerali laboratuvar ortamında üretilip çeşitli işlemlerden sonra kullanıma hazır hale getirilmiştir. Vollastonit katkılı KYG harç üretiminde 0.5 sabit alkali/uçucu kül oranı kullanılmıştır. Alkali oranları (Na2SiO3/NaOH) 1.5, 2 ve 2.5; vollastonit oranları ise %0, %4, %8 ve %12 olarak belirlenmiştir. Geopolimer harçlar 24 saat boyunca 80 oC ve 100 oC sıcaklıklarında kürlenmiştir. Taze haldeyken yayılma çapı ve reoloji değerleri belirlenen geopolimer harçların 28. gün sonunda, eğilme dayanımı, basınç dayanımı, elastisite modülü, UTH, kılcallık ve çeşitli fiziksel değerleri ölçülmüştür. Deney sonuçlarına göre vollastonitin KYG harcın mekanik, durabilite ve fiziksel özelliklerini iyileştirmesinin yanında bazı olumsuz sonuçlara da sebep olduğu gözlemlenmiştir. En iyi basınç dayanımı değeri 100 oC'de kürlenmiş KYG-1.5-8 karışımdan ve en yüksek eğilme dayanımı değeri ise 80 oC'de kürlenmiş KYG-2-12 karışımdan elde edildiği tespit edilmiştir.
dc.description.abstractIn this thesis, fresh, mechanical and physical properties of self-compacting geopolymer (SCG) mortars with wollastonite were investigated at different curing temperatures. SCG was designed with F class fly ash as a binder via activating by sodium silicate and sodium hydroxide solutions. In the first stage of the study, synthetic wollastonite mineral was produced in the laboratory. A fixed alkali/fly ash ratio of 0.5 was used in the production of SCG with wollastonite additive. Alkali ratios (Na2SiO3 / NaOH) were determined as 1, 1.5 and 2, wollastonite ratios were utilized as 0%, 4%, 8% and 12% by the weight binder. Geopolymer mortars were cured at 80 oC and 100 oC for 24 hours. After observing the slump flow diameter and rheology values of SCG incorporating with wollastonite at fresh state, compressive strength, flexural strength, modulus of elasticity, UPV, capillarity and various physical values were measured at the end of the 28th day. According to the results, it was observed that whereas wollastonite was not only improved the mechanical, durability and but also it deteriorated the physical properties of SCG. The highest compressive strength value was obtained from the mixture of SCG-1.5-8 cured at 24 hours, respectively 100 oC while 6.5 MPa was measured as the highest flexural strength for the mixture of SCG-2-12 cured at 80 oC.
dc.identifier.endpage99
dc.identifier.startpage1
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=sELqxhTlFGAjsbjOuuiyCPDjKjKij-8a_NZQQCDBlxFRtzu5tJOZuWISj6zUpKvU
dc.identifier.urihttps://hdl.handle.net/11480/9357
dc.identifier.yoktezid741375
dc.language.isotr
dc.publisherNiğde Ömer Halisdemir Üniversitesi
dc.relation.publicationcategoryTez
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_2024
dc.subjectİnşaat Mühendisliği
dc.subjectCivil Engineering
dc.titleVollastonit katkılı kendiliğinden yerleşen geopolimerin taze ve mekanik özelliklerinin deneysel olarak incelenmesi
dc.title.alternativeExperimental investigation of the fresh and mechanical properties self-compacting geopolymer with wollastonite
dc.typeMaster Thesis