Yeni tip korozyon inhibitörü sentezi, karakterizasyonu ve asidik ortamda yumuşak çeliğin korunması üzerine etkilerinin incelenmesi

Basit Öğe Kaydı
dc.contributor.advisorÖzkır, Demet
dc.contributor.authorBay, Yasemin
dc.date.accessioned2024-11-04T20:07:54Z
dc.date.available2024-11-04T20:07:54Z
dc.date.issued2023
dc.departmentNiğde ÖHÜ, Fen Bilimleri Enstitüsü, Kimya Ana Bilim Dalı
dc.descriptionFen Bilimleri Enstitüsü, Kimya Ana Bilim Dalı
dc.description.abstractBu tez çalışmasında, yeşil bir korozyon inhibitörü olarak kondensasyon tepkimesi ile literatüre göre yeni bir Schiff bazı sentezlenmiş ve bileşiğin yapısı FT-IR ve 1H-NMR analizleriyle aydınlatılmıştır. Bu yeni tip Schiff bazının uygulanabilirliğini test etmek amacıyla, 1,0 M HCl çözeltisindeki yumuşak çeliğin korozyon davranışına inhibitör etkisi bazı elektrokimyasal yöntemlerle araştırılmıştır. Ölçümlerde inhibitör olarak 1,0x10–5 M–1,0x10–3 M Schiff bazı içeren ve içermeyen 1,0 M HCl çözeltileri kullanılmıştır. Bu çözeltilerle 298 K'de bir saat daldırma süresi sonunda EIS, LPR ve potansiyodinamik polarizasyon ölçümleri yapılmıştır. Yeni Schiff bazının hem kısa hem de uzun daldırma sürelerinde etkin olduğu görülmüştür. Hidroklorik asitli ortamdaki yumuşak çeliğin korozyonunu, yeşil inhibitör olarak sentezlenen Schiff bazının önleme etkisi ayrıca FE-SEM ve AFM yüzey analiz teknikleriyle incelenmiştir. Yüzey analizleri sonucunda, elektrot yüzeyinde korozyona karşı koruyucu bir film tabakası oluştuğu net bir şekilde gözlenmiştir. Hem elektrokimyasal deney sonuçları hem de yüzey analiz bulguları birbiriyle son derece uyumlu olmuştur. Bu çalışma ile sentezlenen yeni Schiff bazı, asidik ortamdaki yumuşak çelik için başarılı bir inhibitör olarak uygulanmıştır.
dc.description.abstractIn this thesis, a new Schiff base was synthesized as a green corrosion inhibitor by condensation reaction according to the literature and the structure of the compound was elucidated by FT-IR and 1H-NMR analyses. In order to test the applicability of this new type of Schiff base, the inhibitory effect on the corrosion behavior of mild steel in 1.0 M HCl solution was investigated by some electrochemical methods. In the measurements, 1.0 M HCl solutions with and without 1,0x10–5 M–1,0x10–3 M Schiff base were used as inhibitor. EIS, LPR and potentiodynamic polarization measurements were performed with these solutions after one hour of immersion at 298 K. The new Schiff base was found to be effective in both short and long immersion times. The inhibition effect of Schiff base, which is synthesized as a green inhibitor, on the corrosion of mild steel in HCl solution was also investigated by FE-SEM and AFM surface analysis techniques. As a result of the surface analysis, it was clearly observed that a protective film layer against corrosion was formed on the metal surface. Both the electrochemical test and the surface analysis results were highly compatible with each other. The new Schiff base synthesized in this study was successfully applied as an inhibitor for mild steel in acidic medium.
dc.identifier.endpage78
dc.identifier.startpage1
dc.identifier.urihttps://tez.yok.gov.tr/UlusalTezMerkezi/TezGoster?key=a0OMTmEd_3mfOBxT8SiBTEShq473aQQWeDq_nGHHS_hGVCnaxcVAXShOjWCUEjdt
dc.identifier.urihttps://hdl.handle.net/11480/9500
dc.identifier.yoktezid817375
dc.language.isotr
dc.publisherNiğde Ömer Halisdemir Üniversitesi
dc.relation.publicationcategoryTez
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_2024
dc.subjectKimya
dc.subjectChemistry
dc.titleYeni tip korozyon inhibitörü sentezi, karakterizasyonu ve asidik ortamda yumuşak çeliğin korunması üzerine etkilerinin incelenmesi
dc.title.alternativeSynthesis, characterization of new type corrosion inhibitor and examination of its protection effect on mild steel in acidic medium
dc.typeMaster Thesis