Optical spectroscopy of the Ce-doped multicomponent garnets
Küçük Resim Yok
Tarih
2016
Dergi Başlığı
Dergi ISSN
Cilt Başlığı
Yayıncı
PERGAMON-ELSEVIER SCIENCE LTD
Erişim Hakkı
info:eu-repo/semantics/closedAccess
Özet
Here, we report our results referring to the preparation of Ce doped Y2.22MgGa2Al2SiO12, Y1.93MgAl4SiO12 and Y2.22Gd0.75Ga2Al3O12 using solid state reaction at high temperature. Several complementary methods (i.e. powder x-ray diffraction (XRPD), energy dispersive analysis of X-rays (EDX), scanning electron microscopy (SEM) and Fourier transforms infrared spectroscopy (FTIR)) were studied to examine the effects of the synthesis procedure on the morphology and structure. XRD analyses revealed that all compounds include yttrium aluminate phase with garnet structure. Cathodoluminescence (CL), radioluminescence (RL) and photoluminescence (PL) measurements were carried out for clarification of relationship between host lattice defects and the spectral luminescence emissions. Luminescence emission of phosphors is peaked at 530 nm assigned to 5d-4f transitions of the dopant Ce3+ ions with a broad emission band in 400-700 nm range. Under electron irradiation, the emission spectrum of Ce doped (YGd)(3)Ga2Al3O12 is well defined and has a characteristic fairly narrow and sharp emission band peaking at 312 nm and 624 nm corresponding to transition of P-6(7/2) -> S-8(7/2) and (6)G(J) -> P-6(J) (Gd3+), respectively. We suggest some of phosphors might be excellent phototherapy phosphor materials under electron excitation. (C) 2016 Elsevier Ltd. All rights reserved.
Açıklama
Anahtar Kelimeler
Yttrium aluminate, Rare earth, XRD, FTIR, Luminescence
Kaynak
APPLIED RADIATION AND ISOTOPES
WoS Q Değeri
Q3
Scopus Q Değeri
Q3
Cilt
114