Türkiye De Çıkartılan Opal (SiO2 nH2O) Minerallerinin Termolüminesans Özelliklerinin İncelenmesi

Basit Öğe Kaydı
dc.contributor.advisorCanımoğlu, Adil
dc.contributor.authorYürek, Hasan
dc.date.accessioned2014-09-16T10:21:03Z
dc.date.available2014-09-16T10:21:03Z
dc.date.issued2013
dc.departmentNiğde ÖHÜ, Fen Bilimleri Enstitüsü, Fizik Ana Bilim Dalı
dc.description.abstractBu çalışmada, dozimetre olarak tasarlanan opal kristallerinin termolüminesans özellikleri çalışıldı. Opal kristallerine radyasyon işlemi uygulanmadan önce, yeşil opal ve süt opal kristallerinin oda sıcaklığında 200nm-800nm dalga boyu aralığında optik soğurma grafikleri UV-VIS-IR spektrofotometre ile elde edildi. Daha sonra kristaller ayrı ayrı 100, 200, 300, 400, 500 ve 6000C sıcaklık değerlerinde tavlandıktan sonra onların tekrar soğurma eğrileri elde edildi. Diğer taraftan, opal kristallerine radyasyon uygulanmadan önce, kristallerin TL parıldama eğrileri ß= 20C/s ısıtma oranı için elde edildi. Benzer işlemler uygulanan 150, 300, 450, 600 ve 750Gy?25dk farklı X-ışını dozlarına maruz bırakılarak opal kristallerinin TL parıldama eğrileri elde edildi. Bu ölçümler 500C-4000C sıcaklık aralığında gerçekleştirildi. Sabit ısıtma oranı için elde edilen parıldama eğrileri kullanılarak verilen doz miktarı ile TL şiddeti arasındaki ilişkiler araştırıldı. Oluşan grafiklerden yeşil opal ve süt opal arasındaki ilişkiler incelendi, elde edilen grafiklerden yeşil opalde üç pik oluşurken süt opalde tek pik oluştuğu gözlendi
dc.description.abstractIn this study, the thermoluminescence properties of opal crystals designed as dosimeter were studied. Before radiation process was applied, absorption graphics of green opal and milk opal crystals were obtained in the wavelength range 200 nm and 800 nm at room temperature. Then, after every crystal was annealed at 100, 200, 300, 400, 500 and 6000C its absorption curves were obtained corresponding these temperatures. On the other hand, before radiation is not exposed to opal crystals, their TL glow curves were obtained for a heating rate ß= 20C/s. After this, every opal crystal was exposed to 150, 300, 450, 600 and 750Gy?25min X-ray doses and its TL glow curves were obtained. These measurement, were carried out in the temperature range 500C-4000C. The relationship between the applied dose amount and TL intensity are investigated using the TL glow curves obtained at constant heating rate. When the graphics obtained for green opal crystals and milk opal crystals were compared with each other, it was observed that three peaks appeared on the green opal curves while one peak was appearing on the milk opal curves …
dc.identifier.urihttps://hdl.handle.net/11480/387
dc.identifier.yoktezid332254
dc.institutionauthorYürek, Hasan
dc.language.isotr
dc.publisherNiğde Üniversitesi
dc.relation.publicationcategoryTez
dc.rightsinfo:eu-repo/semantics/openAccess
dc.subjectOpal
dc.subjectOpalin Tavlanması
dc.subjectDozimetre
dc.subjectTermolüminesans
dc.titleTürkiye De Çıkartılan Opal (SiO2 nH2O) Minerallerinin Termolüminesans Özelliklerinin İncelenmesi
dc.typeMaster Thesis

Dosyalar

Orijinal paket
Listeleniyor 1 - 1 / 1
Küçük Resim
İsim:
TÜRKİYE’DE ÇIKARTILAN OPAL (SiO2 nH2O) MİNERALLERİNİN TERMOLÜMİNESANS ÖZELLİKLERİNİN İNCELENEMESİ.pdf
Boyut:
2.08 MB
Biçim:
Adobe Portable Document Format
Açıklama:
TEZ
İndir
Lisans paketi
Listeleniyor 1 - 1 / 1
Küçük Resim Yok
İsim:
license.txt
Boyut:
1.44 KB
Biçim:
Item-specific license agreed upon to submission
Açıklama:
İndir

Koleksiyon

Fen Bilimleri Enstitüsü Tez Koleksiyonu