Enhancement of Shear Strength in Lap Joints with Different Surface Patterns

Küçük Resim Yok

Tarih

2023

Dergi Başlığı

Dergi ISSN

Cilt Başlığı

Yayıncı

Erişim Hakkı

info:eu-repo/semantics/openAccess

Özet

In this study, surface patterning with CNC vertical machining center was applied to aluminum surface for the enhancement of the shear strength of the epoxy bonded lap joints. It was found that the pattern shape affected shear strength and among vertical, square, horizontal, 45 degree and diamond patterns, 45 degree provided the highest shear strength of 24.6 MPa. Moreover, the pattern features also affected the shear strength. Decrease in the depth led to slightly lower shear strength, whereas increase in the depth gave slight enhancement. The optimum depth was found as 300 ?m and the obtained shear strength was calculated as 25.5 MPa. Additionally, increase in the width length led to lower shear strength. On the other hand, decrease in the width length provided higher shear strength. The increment became smaller as the width length increased. Also, after a point, the trend reversed and the shear strength decrease slightly. The optimum width length and the corresponding shear strength were found as 1.0 mm and 28.0 MPa, respectively.

Açıklama

Anahtar Kelimeler

Malzeme Bilimleri, Özellik ve Test, Malzeme Bilimleri, Kaplamalar ve Filmler, İmalat Mühendisliği, Mühendislik, Kimya, CNC, Epoxy, Shear strength, Lap joint, Surface pattern

Kaynak

Osmaniye Korkut Ata Üniversitesi Fen Bilimleri Enstitüsü Dergisi (Online)

WoS Q Değeri

Scopus Q Değeri

Cilt

6

Sayı

2

Künye