Surface coating of micronized calcite (CaCO3) with stearic acid via an attritor mill

Basit Öğe Kaydı
dc.contributor.authorEhsan, Ahmad Farid
dc.contributor.authorToraman, Öner Yusuf
dc.date.accessioned2024-11-07T13:16:46Z
dc.date.available2024-11-07T13:16:46Z
dc.date.issued2024
dc.departmentNiğde Ömer Halisdemir Üniversitesi
dc.description.abstractIn this study, the surface coating (modification) of micronized calcite (CaCO3, d50=135 ?m) in a stirred media (bead) mill with stearic acid was investigated. As a result of 15 min grinding and 5 min coating experiments, a product with d50=2.15 ?m and specific surface area of 3.21 m2/cm3 was obtained. The activation rate of this final product as an indicator of coating rate was 97.7%. According to the optimum coating results, the stearic acid rate was determined as 1%, the modification time was 7.5 min, the ball load was 900 g and the stirring speed was 600 rpm.
dc.identifier.doi10.28948/ngumuh.1390147
dc.identifier.endpage765
dc.identifier.issn2564-6605
dc.identifier.issue3
dc.identifier.startpage760
dc.identifier.trdizinid1249719
dc.identifier.urihttps://doi.org/10.28948/ngumuh.1390147
dc.identifier.urihttps://search.trdizin.gov.tr/tr/yayin/detay/1249719
dc.identifier.urihttps://hdl.handle.net/11480/12562
dc.identifier.volume13
dc.indekslendigikaynakTR-Dizin
dc.language.isoen
dc.relation.ispartofNiğde Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi
dc.relation.publicationcategoryMakale - Ulusal Hakemli Dergi - Kurum Öğretim Elemanı
dc.rightsinfo:eu-repo/semantics/openAccess
dc.snmzKA_20241107
dc.subjectNanobilim ve Nanoteknoloji
dc.subjectMalzeme Bilimleri
dc.subjectTekstil
dc.subjectMalzeme Bilimleri
dc.subjectÖzellik ve Test
dc.subjectMalzeme Bilimleri
dc.subjectKâğıt ve Ahşap
dc.subjectMalzeme Bilimleri
dc.subjectKaplamalar ve Filmler
dc.subjectMalzeme Bilimleri
dc.subjectBiyomalzemeler
dc.subjectMalzeme Bilimleri
dc.subjectSeramik
dc.subjectMalzeme Bilimleri
dc.subjectKompozitler
dc.subjectSurface modification
dc.subjectCalcite
dc.subjectStearic acid
dc.subjectDry coating
dc.subjectActive ratio
dc.titleSurface coating of micronized calcite (CaCO3) with stearic acid via an attritor mill
dc.typeArticle

Dosyalar

Koleksiyon

TR-Dizin İndeksli Yayınlar Koleksiyonu
Ömer Halisdemir Üniversitesi Mühendislik Bilimleri Dergisi Koleksiyonu