Doğal vollastonitin yüksek performanslı harç üzerine etkileri

Malkoç, Beytullah

Doğal vollastonitin yüksek performanslı harç üzerine etkileri

dc.contributor.advisor	Öz, Hatice Öznur
dc.contributor.author	Malkoç, Beytullah
dc.date.accessioned	2021-08-02T06:05:51Z
dc.date.available	2021-08-02T06:05:51Z
dc.date.issued	2020
dc.date.submitted	2020-01
dc.department	Niğde ÖHÜ, Fen Bilimleri Enstitüsü, İnşaat Mühendisliği Ana Bilim Dalı
dc.description.abstract	Bu çalışma kapsamında doğal vollastonit yüksek performanslı harçta değişen oranlarda çimento ile yer değiştirilerek doğal vollastonitin yüksek performanslı harçta dayanım ve kalıcılık üzerindeki etkileri araştırılmıştır. Yüksek performanslı harç üretim aşamasında su/bağlayıcı oranı sabit tutularak vollastonit minerali %3, %6, %9, %12 ve %15 oranlarında karışıma eklenmiştir. Ayrıca su azaltıcı katkı maddesi olan süper akışkanlaştırıcı vasıtasıyla karışımın akıcılığı sağlanmıştır. Üretim aşamasında ilk etapta karışımda vollastonit kullanılmadan kontrol harcı üretilmiş, sonraki üretim aşamalarında ise yukarıdaki oranlarda vollastonit minerali çimento ile yer değiştirecek şekilde karışıma ilave edilmiştir. Üretilen numuneler bir günlük kalıplama süresinin ardından kür havuzlarına alınmıştır. Basınç, eğilme ve ultrasonik titreşim hızı testleri 3., 7., 28 ve 90. günlerde yapılırken, kılcal su geçirimliliği ve gaz geçirimliliği deneyleri 28. ve 90. günde ölçülmüştür. Bu deneylerden elde edilen sonuçlara göre %3 vollastonit içeren karışımlarda tüm deneyler için performansta iyileşme gözlenmiştir. %6 vollastonit içeriğine sahip karışımlarda ise kontrol harcına oranla daha iyi sonuçlar alınırken %3 vollastonit içeren karışıma göre performansta azalmalar gözlenmiştir. Vollastonit kullanımıyla performansta yaşanan iyileşmenin sebebi bu mineralin sahip olduğu iğnemsi yapı ve yüksek elastisite modülüyle açıklanabillir.
dc.description.abstract	In this study, the effects of natural wollastonite on the strength and permanence of high performance concrete (HPC) were investigated. In the high performance mortar production, wollastonite mineral was added to the mixture at 3%, 6%, 9%, 12% and 15% by keeping the water/binder ratio constant. In addition, the workability of the mixture was achieved by means of the superplasticizer, a water reducing admixture. In the first stage of the production, control mortar was utilized without using wollastonite in the mixture. After one day of molding, the samples were taken to curing ponds. Compressive, flexural and ultrasonic pulse velocity tests were conducted at 3,7, 28 and 90 days while sorptivity and gas permeability test were measured at 28 and 90 days. According to the obtained results of these experiments, the performance increment of mixture containing 3% wollastonite was observed for all experiments. Considering the mixtures containing 6% wollastonite, better results was obtained as against the control group where the decrement in performance is observed with the comparison of the mixture containing 3% wollastonite. The improvement of the performance with the use of wollastonite can be explained with it's acicular structure and high modulus of elasticity.
dc.identifier.citation	Malkoç, B. (2020). Doğal vollastonitin yüksek performanslı harç üzerine etkileri. (Yüksek Lisans Tezi) Niğde Ömer Halisdemir Üniversitesi, Fen Bilimleri Enstitüsü, Niğde
dc.identifier.uri	https://hdl.handle.net/11480/7657
dc.identifier.yoktezid	620454
dc.language.iso	tr
dc.publisher	Niğde Ömer Halisdemir Üniversitesi / Fen Bilimleri Enstitüsü
dc.relation.publicationcategory	Tez
dc.rights	info:eu-repo/semantics/openAccess
dc.subject	Vollastonit
dc.subject	Yüksek performanslı harç
dc.subject	Yüksek dayanım
dc.subject	Durabilite
dc.subject	Wollastonite
dc.subject	High performance mortar
dc.subject	High strength
dc.subject	Durability
dc.title	Doğal vollastonitin yüksek performanslı harç üzerine etkileri
dc.title.alternative	The effects of natural wollastoni?te on high performance mortars
dc.type	Master Thesis